TINOX TPW-716 is an advanced hybrid pigment based on rutile-type TiO₂, engineered specifically for high-performance paint and coating applications. Through a proprietary manufacturing process that combines premium TiO₂ pigment components with ultra-fine functional fillers, TPW-716 enhances light scattering efficiency while reducing TiO₂ consumption without compromising optical performance.

• Superior Optical Properties Brightness L* ≥ 96.0 with bluish undertone for exceptional whiteness and visual appeal
• Excellent Gloss Development Enhanced surface reflectivity and gloss stability for premium finishes
• Strong Hiding Power Outstanding coverage with reduced pigment loading requirements
• Enhanced Durability Improved abrasion resistance, weather resistance, and coating film hardness
• Excellent Dispersion Hegman ≥ 6.5 for easy incorporation and reduced processing time
• Environmental Benefits Lower CO₂ emissions per unit compared to pure TiO₂

• Whiteness index nearly matching premium TiO₂ pigment R-2160
• Superior performance compared to standard TiO₂ pigment R-2140
• Excellent opacity levels comparable to pure TiO₂ pigments
• Outstanding gloss development for high-quality finishes

1. Add water, dispersing agent, and wetting agent to mixing vessel
2. Slowly add TINOX TPW-716 under moderate agitation (800-1000 rpm)
3. Increase agitation speed to 1500-2000 rpm for 15-20 minutes until Hegman fineness ≥6.5 is achieved
4. Reduce speed and slowly add acrylic emulsion
5. Add coalescing agent, defoamer, rheology modifier, and preservative
6. Adjust pH to 7.5-8.5 with ammonia solution
7. Add remaining water to achieve desired viscosity
8. Filter and package

• Whiteness Index: ≥96.5
• Gloss (60°): ≥85 GU
• Contrast Ratio: ≥0.98
• Yellowness Index: <1.5
• PVC: ~25%

Note: This formulation is based on test data from the TINOX TPW Series brochure, specifically the acrylic enamel paint tests with 75% emulsion content (PVC = 25%).